| Mekanik Özellikleri Minimum Değerler MPA | Sertlik HRB |
Korozyon Dayanımı | Kaynak Etkisi |
Soğuk Şekil Alma |
Kaynak Edilebilme |
AST | |||||
| Akma %0.2 Rp 0.2 |
Akma %1 Rp 1 |
Çekme Rm |
Uzama A5 |
Genel | Pitting | Oksidasyon | |||||
| 260 210 210 200 |
290 250 250 240 |
600-950 550-750 550-750 520-670 |
40 45 45 45 |
92 92 92 92 |
+ ++ ++ ++ |
+ ++ ++ ++ |
++ ++ ++ ++ |
- | ++ +++ +++ +++ |
++ +++ +++ +++ |
301 304 D 304 PS 304 L |
| 210 240 240 230 |
250 270 270 260 |
520-670 540-740 540-740 500-750 |
45 35 35 35 |
90 88 88 94 |
++ ++ ++ + |
++ | ++ +++ +++ +++ |
- | ++ + + + |
+++ +++ ++ +++ |
321 309 S 310 S 4828 |
| 210 210 210 |
250 250 250 |
550-700 540-690 550-700 |
45 45 40 |
90 90 90 |
+++ +++ +++ |
+++ +++ +++ |
+ + + |
- - |
++ +++ ++ |
+++ +++ +++ |
316 316 L 316 Tİ |
| 210 300 |
380-520 0-800 |
30 15 |
88 99 |
· · |
· · |
· · |
- · |
+++ · |
++ · |
409 LI 420 |
|
| 270 270 205 |
450-600 450-550 450-600 |
20 24 24 |
89 89 89 |
+ + + |
+ ++ + |
+ + + |
- - |
+++ +++ ++ |
+ ++ ++ |
430 430 Tİ 430 Cb |
|
| 260 270 |
450-630 450-550 |
27 28 |
89 89 |
++ + |
++ ++ |
+ ++ |
- | +++ ++ |
+ ++ |
436 LI 441 LI |
|
- etkisiz veya çok az etkisi var
· gerekli değil veya uygulanamaz
+ kabul edilebilir dayanım ++ iyi dayanım +++ çok iyi ++++ bu
özelliği artırmak için geliştirilmiş
 |
 |
 |
|
 |