| AST | %C | %Cr | %Ni | %Si | %Mn | Diğer % |
|||||
| min | max | min | max | min | max | min | max | min | max | ||
| 301 304 D 304 PS 304 L |
0.090 040 |
0.120 0.060 0.060 0.030 |
16.00 18.00 18.00 18.00 |
18.00 20.00 20.00 20.00 |
6.00 8.50 9.00 10.00 |
8.00 10.50 10.50 12.00 |
0.75 0.75 0.75 0.75 |
2.00 2.00 2.00 2.00 |
N0.10 max |
||
| 321 309 S 310 S 4288 |
0.060 0.080 0.080 0.080 |
17.00 22.00 24.00 19.00 |
19.00 24.00 26.00 21.00 |
9.00 12.00 19.00 11.00 |
12.00 15.00 22.00 13.00 |
1.50 | 0.75 0.75 1.50 2.50 |
0.90 | 2.00 2.00 2.00 2.00 |
Ti5X(C+N)min, 0.70 max | |
| 316 316 L 316 Tİ |
0.060 0.030 0.060 |
16.50 16.50 16.50 |
18.00 18.00 18.00 |
10.50 11.00 11.00 |
13.00 14.00 14.00 |
0.75 0.75 0.75 |
2.00 2.00 2.00 |
Mo 2.00-2.50 N 0.10 max Mo 2.00-2.50 N 0.10 max Ti5X(C+N)min, 0.60 max N 0.10max Mo 2.00-2.50 |
|||
| 409 LI 420 |
0.420 | 0.025 0.500 |
10.50 12.50 |
11.75 14.00 |
0.50 0.75 |
0.80 0.75 |
1.00 1.00 |
Ti6(C+N)min, 0.60max | |||
| 430 430 Tİ 430 Cb |
0.080 0.060 0.060 |
16.00 16.00 16.00 |
17.50 17.50 17.50 |
0.75 0.75 0.75 |
0.75 0.75 0.75 |
0.75 0.75 0.75 |
Ti ³ 7XC £
0.60 Cb ³ 13XC £ 1.00 |
||||
| 436 LI 441 LI |
0.030 0.030 |
17.50 17.50 |
19.00 19.00 |
0.50 0.50 |
0.75 0.75 |
0.80 0.50 |
Mo 0.90-1.25 Cu 0.30-0.7 Ti+Nb ³ 10(C+N) Nb 0.30-1.00 Ti 0.10-0.30 |
||||
 |
 |
 |
|
 |